482 :名前なカッター(ノ∀`) (ワッチョイ 6524-8H9x)[]:2020/04/05(日) 08:06:19.23 ID:ohAaor0v0 - マイクスチュアートがm390をバークリバーで出さない理由
Mike Stewart 2019/01/21 We have covered this many times - M390 IS chippy as Hell - so is 20CV and 204P. Edge Holding - Supreme - Toughness - In the Basement. It might be a Grail steel for a folder but it is a wrong Choice for a fixed Blade that will see use beyond guarding stuff in your sock Drawer. We have made three knives in 20CV - it is the very same steel as M390. They come back all the time Chipped - the Chef knives we made from 20Cv are fine as long as you don't side Stress it - Guess What ??? - A Couple of People have Side Stressed them - Boom - Broken in Half. You will not be seeing us use those Steels unless we ever make a folder and i'm not even sure i would use it then. It ain't no Grail steel to me. All of those Steels that are Extreme edge holding lack the Balance of Edge holding and toughness - We don't sacrifice Toughness for Edge Holding here. You can sharpen a dull knife - you are screwed if you are outr in the field - in a tough Spot - and your knife Breaks.
|
|